Electrodeposition of CuIn1-xGaxSe2 solar cells with a periodically-textured surface for efficient light collection

Chia Lung Tsai*, Kuo Min Huang, Ming Jer Jeng

*Corresponding author for this work

Research output: Contribution to journalJournal Article peer-review

3 Scopus citations

Abstract

The photoresponse of CuIn1-xGaxSe2 (CIGS) solar cells is improved using a periodically-textured structure as an antireflection layer. The CIGS absorber layers were prepared by one-step electrodeposition from an aqueous solution containing 12 mM CuSO4, 25 mM In2(SO4)3, 28 mM Ga2(SO 4)3, and 25 mM SeO2. The electrodeposited CIGS films exhibit the (112)-preferred orientation of the chalcopyrite structures and feature improved film stoichiometry after the selenization process. In addition, the lower bandgap value of 0.97 eV is caused by the discrepancy of the reduction potentials for each constituent, resulting in insufficient Ga content in the deposited films. Using self-assembled silica nanoparticles as the etching mask, periodically-textured structures can be easily formed on an indium tin oxide (ITO)-coated soda lime glass to achieve a low average reflection (<10.5%) in a wide wavelength and incident angle range. With the periodic textured structures suppressing light reflections from the front surface, the photogenerated current in the semi-transparent CIGS solar cells made with transparent conducting electrodes is 1.82 times higher than they otherwise would be.

Original languageEnglish
Pages (from-to)1599-1602
Number of pages4
JournalMaterials Science in Semiconductor Processing
Volume16
Issue number6
DOIs
StatePublished - 2013

Keywords

  • Antireflection layer
  • CuInGaSe
  • Electrodeposition
  • Self-assembled nanoparticles
  • Solar cells

Fingerprint

Dive into the research topics of 'Electrodeposition of CuIn1-xGaxSe2 solar cells with a periodically-textured surface for efficient light collection'. Together they form a unique fingerprint.

Cite this