Enhancing Bone Regeneration Using Blended Poly(L-lactide-co-D, L-lactide) and β-Tricalcium Phosphate Nanofibrous Periodontal Biodegradable Membranes

In regenerative periodontal treatment, barrier membranes restore periodontal support and aid tissue healing, but slow hard tissue regeneration can disrupt healing and cause tooth instability. This study aimed to fabricate a periodontal membrane through electrospinning poly(L-lactide-co-D, L-lactide) with varying β-tricalcium phosphate (β-TCP) percentages (0%, 10%, 30%, and 40%) treated with hyaluronic acid to enhance bone regeneration in alveolar bone defects. Their ability to promote biomimetic mineralization was characterized using field emission scanning electron microscopy (FESEM) analysis, wettability, and mechanical properties. Biocompatibility and osteogenic differentiation were evaluated by examining BMSCs’ behavior. In vivo, the PLA/β-TCP membrane’s potential to promote bone regeneration was assessed through CT imaging and histological examination. FESEM analysis revealed β-TCP agglomerations within PLA fibers, increasing tensile strength. Water contact angle measurements showed better wettability and higher cell viability after hyaluronic acid treatment, indicating non-cytotoxicity. Membranes with 10% and 30% (w/w) β-TCP significantly enhanced cellular activities, including proliferation and osteogenic differentiation. Animal tests showed a significant bone growth rate increase to 28.9% in the experimental group compared to 24.9% with the commercial product Epi-Guide after three months. Overall, PLA with 30% β-TCP optimally promoted periodontal hard tissue repair and potentially enhanced bone regeneration.