TY - JOUR
T1 - In vitro and in vivo osteogenesis of gelatin-modified calcium silicate cement with washout resistance
AU - Wu, I. Ting
AU - Kao, Pan Fu
AU - Huang, Yun Ru
AU - Ding, Shinn Jyh
N1 - Publisher Copyright:
© 2020 Elsevier B.V.
PY - 2020/12
Y1 - 2020/12
N2 - The purpose of this study was to evaluate the physicochemical properties and the in vitro and in vivo osteogenesis of the newly developed calcium silicate containing 5 wt% gelatin (CSG) cement compared with calcium silicate (CS) and calcium sulfate hemihydrate (CSH) cements. In addition to the phase composition and microstructure, washout resistance, setting time, and diametral tensile strength of the bone cements were also performed. In vitro examination of cell growth, differentiation, and mineralization were performed with macrophage cell line (RAW 264.7), MG63 human osteoblast-like cells, and human mesenchymal stem cells (hMSCs). The mini-pig model with mandibular alveolar bone defect was used to assess the in vivo function of cement. Histological and histomorphometric assessments were performed at 6 and 12 weeks after implantation. The results indicated that the CS and CSG powders were mainly composed of poorly crystalline β-dicalcium silicate, and the irregular CSH powders had a highly crystalline phase. After setting, the product of CS and CSG was calcium-silicate-hydrate gel and CSH exhibited a plate-like gypsum crystal structure. The setting time of CS, CSG, and CSH was 19, 35, and 10 min, respectively. Gelatin effectively improved the washout resistance and diametral tensile strength of CS from 2.4 MPa to 3.4 MPa, while CSH had no washout resistance and its strength was 7.6 MPa. The osteogenic activity of MG63 and hMSC cells on the CSG cement surface was consistently shown to be significantly higher than that on the CSH cement surface. Interestingly, CS and CSG cements exhibited lower macrophage expression compared to CSH cements. Twelve week after implantation, the amount of new bone in the defect area of the CS group was slightly higher than that of the CSG and CSH groups. It is concluded that CSG cement had improved anti-washout performance, favorable osteogenesis in vitro and in vivo, which was beneficial for clinical application.
AB - The purpose of this study was to evaluate the physicochemical properties and the in vitro and in vivo osteogenesis of the newly developed calcium silicate containing 5 wt% gelatin (CSG) cement compared with calcium silicate (CS) and calcium sulfate hemihydrate (CSH) cements. In addition to the phase composition and microstructure, washout resistance, setting time, and diametral tensile strength of the bone cements were also performed. In vitro examination of cell growth, differentiation, and mineralization were performed with macrophage cell line (RAW 264.7), MG63 human osteoblast-like cells, and human mesenchymal stem cells (hMSCs). The mini-pig model with mandibular alveolar bone defect was used to assess the in vivo function of cement. Histological and histomorphometric assessments were performed at 6 and 12 weeks after implantation. The results indicated that the CS and CSG powders were mainly composed of poorly crystalline β-dicalcium silicate, and the irregular CSH powders had a highly crystalline phase. After setting, the product of CS and CSG was calcium-silicate-hydrate gel and CSH exhibited a plate-like gypsum crystal structure. The setting time of CS, CSG, and CSH was 19, 35, and 10 min, respectively. Gelatin effectively improved the washout resistance and diametral tensile strength of CS from 2.4 MPa to 3.4 MPa, while CSH had no washout resistance and its strength was 7.6 MPa. The osteogenic activity of MG63 and hMSC cells on the CSG cement surface was consistently shown to be significantly higher than that on the CSH cement surface. Interestingly, CS and CSG cements exhibited lower macrophage expression compared to CSH cements. Twelve week after implantation, the amount of new bone in the defect area of the CS group was slightly higher than that of the CSG and CSH groups. It is concluded that CSG cement had improved anti-washout performance, favorable osteogenesis in vitro and in vivo, which was beneficial for clinical application.
KW - Bone cement
KW - Bone repair
KW - Calcium silicate
KW - Calcium sulfate
KW - Gelatin
UR - http://www.scopus.com/inward/record.url?scp=85089234712&partnerID=8YFLogxK
U2 - 10.1016/j.msec.2020.111297
DO - 10.1016/j.msec.2020.111297
M3 - 文章
C2 - 32919658
AN - SCOPUS:85089234712
SN - 0928-4931
VL - 117
JO - Materials Science and Engineering C
JF - Materials Science and Engineering C
M1 - 111297
ER -