Fracture resistance and marginal discrepancy of porcelain laminate veneers influenced by preparation design and restorative material in vitro

Tai Min Lin, Perng Ru Liu, Lance C. Ramp, Milton E. Essig, Daniel A. Givan, Yu Hwa Pan*

*此作品的通信作者

研究成果: 期刊稿件文章同行評審

53 引文 斯高帕斯(Scopus)

摘要

Objectives: The purpose of this investigation is to evaluate marginal discrepancy and fracture resistance of two veneering materials using two preparation designs. Methods: Two veneer preparation designs (full and traditional) were restored with leucite-reinforced ceramic (ProCAD, Ivoclar Vivadent, Amherst, NY) milled by CAD/CAM (Cerec 3D milling system, Serona Dental Systems), and conventional sintered feldspathic porcelain (Noritake Super Porcelain EX3, Noritake Dental Supply Co). Forty-eight specimens were analysed with a sample size of n = 12 per group. The thickness of each veneer was measured on four specific surfaces. Marginal discrepancy was evaluated with a replica technique and cross-sectional view using a digital microscope. The fracture resistance of veneers cemented on standardised composite resin dies was evaluated using a universal testing machine. Results were analysed with ANOVA, Tukey-Kramer post hoc testing, and linear regression. Results: The results of this investigation revealed no correlation between the thickness and marginal discrepancy of the veneers. The full preparation design with ProCAD and the traditional preparation design with feldspathic porcelain manifested smaller gap. Fracture resistance was decreased for the full preparation design with feldspathic porcelain. Conclusions: In terms of marginal discrepancy and fracture resistance, the most favourable combination was a traditional veneer preparation design with conventional sintered feldspathic porcelain. For the full veneer preparation, a stronger ceramic material such as ProCAD is suggested.

原文英語
頁(從 - 到)202-209
頁數8
期刊Journal of Dentistry
40
發行號3
DOIs
出版狀態已出版 - 03 2012

指紋

深入研究「Fracture resistance and marginal discrepancy of porcelain laminate veneers influenced by preparation design and restorative material in vitro」主題。共同形成了獨特的指紋。

引用此