Nanoarchitectonics of ternary NixCo1-xSe2 electrocatalysts on Ni-foams combined with Pt-loaded carbon clothes as the air-cathodes in Zn-air energy storage systems

Yu Syuan Jheng, Shing Jiang Jessie Lue, Kong Wei Cheng*

*此作品的通信作者

研究成果: 期刊稿件文章同行評審

5 引文 斯高帕斯(Scopus)

摘要

Background: Large-scale application of renewable energy with energy storage system is important for the reduction of influence on global warming effect without decreasing industrial activities. To develop an energy storage system is thus an important way for industrial application. Methods: Ternary NixCo1-xSe2 electrocatalysts were prepared in an ethanol bath with reaction temperature of 70 °C in 10 min using a simple chemical synthesis method. Samples after post-selenization process as the electrocatalysts on nickel (Ni)-foams with Pt-loading carbon clothes were employed in Zn-air batteries. Significant findings: The X-ray diffraction patterns of samples showed ternary NixCo1-xSe2 samples with high Se-vacancies. Therefore, the post-selenization process with temperature of 500 °C for 30 min was applied on these samples with various weights of Se powders. Samples as the electrocatalysts showed good stabilities in our homemade Zn-air batteries with the minimum voltage difference for oxygen evolution/reduction reactions of 0.91 V. Our cell with NiCo1-xSe2 electrocatalyst (Ni:Co:Se=0.21:0.29:0.50)@Ni foam + Pt-loading carbon cloth as the air-cathode showed the charge/discharge voltages of 2.05 and 1.08 V at charge/discharge current density of 10 mA/cm2, respectively, and could be applied in industrial energy storage system.

原文英語
文章編號105451
期刊Journal of the Taiwan Institute of Chemical Engineers
159
DOIs
出版狀態已出版 - 06 2024

文獻附註

Publisher Copyright:
© 2024

指紋

深入研究「Nanoarchitectonics of ternary NixCo1-xSe2 electrocatalysts on Ni-foams combined with Pt-loaded carbon clothes as the air-cathodes in Zn-air energy storage systems」主題。共同形成了獨特的指紋。

引用此