Thickness-dependent optoelectronic properties of CuCr_0.93Mg_0.07O₂ thin films deposited by reactive magnetron sputtering

CuCr_0.93Mg_0.07O₂ thin films were successfully deposited by DC reactive magnetron sputtering at 1123 K from metallic targets. The influence of film thickness on the structural and optoelectronic properties of the films was investigated. X-ray diffraction (XRD) results revealed that all the films had a delafossite structure with no other phases. The optical and electrical properties were investigated by UV–VIS spectrophotometer and Hall measurement, respectively. It was found that the optoelectronic properties exhibited a thickness-dependent behavior. The optical band gap and the average transmittance of the films showed a monotonous decrease with respect to the increase in thickness. The average transmittance in the visible region decreased from 67% to 47% as the thickness increased from ~70 nm to ~280 nm. Simultaneously, the conductivity of the films fell from 1.40 S∙cm⁻¹ to 0.27 S∙cm⁻¹. According to Haacke's figure of merit (FOM), a film with a maximum FOM value of about 1.72×10⁻⁷ Ω⁻¹ can be achieved when the thickness is about 70 nm (σ≈ 1.40 S·cm⁻¹ and T_av. ≈67%).